The light-emitting device consisting of organic white-light components
Chen, Z; Feng, L; Zhang, C; Bie, H; Lei, G; Bai, F
| HERO ID | 3576192 |
|---|---|
| In Press | No |
| Year | 2007 |
| Title | The light-emitting device consisting of organic white-light components |
| Authors | Chen, Z; Feng, L; Zhang, C; Bie, H; Lei, G; Bai, F |
| Journal | Current Opinion in Solid State & Materials Science |
| Volume | 11 |
| Issue | 1-2 |
| Page Numbers | 28-32 |
| Abstract | A material compound, 9,9-bis{4'-[2 ''-(carbazolyl)-vinyl]-phenyl}fluorene (F-CZV), was specially synthesized and used to fabricate the efficient white organic light-emitting devices (WOLEDs). The absorption peaks appear at 340 nm and 346 nm in dilute dichloromethane solution and film, respectively. The photoluminescence peaks appear at 350 nm and 400 nm in the solution and film, respectively. Photoluminescent quantum yield in solution is ca 0.82 by using quinine sulfate as the standard. In an optimized electroluminescent device structure of ITO/NPB (40 nm)/F-CZV (30 nm)/BPhen (40 nm)/Mg:Ag, the saturated white-light emission was observed at Commission International De L'Eclairage (CIE) coordinates of (0.30,0.33) at 10 V. The El spectrum of the device is close to independent of the applied driving voltage. It's maximum brightness and current efficiency is 700 cd/m(2) and 0.41 cd/A, respectively. (C) 2008 Elsevier Ltd. All rights reserved. |
| Doi | 10.1016/j.cossms.2008.04.001 |
| Wosid | WOS:000257649600004 |
| Is Certified Translation | No |
| Dupe Override | No |
| Is Public | Yes |
| Keyword | WOLEDs; F-CZV; photoluminescence; electroluminescent |